XL128 high reinforcing, high abrasion white carbon black
Project
Technical Index
Testing Method
Whiteness
Superior or equivalent
to master standard
HG/T3063-1999（eqv ISO 5794-1:1994）
Silica content(dry)%
≥90
HG/T3062-1999（eqv ISO 5794-1:1994）
Heating loss % 105℃ 2h
4.0-7.0
HG/T3065-1999（eqv ISO 5794-1:1994）
Ignition loss(dry)% 1000℃ 2h
3.0-6.0
HG/T3066-1999（eqv ISO 5794-1:1994）
PH value
6.0-7.5
HG/T3067-1999（eqv ISO 5794-1:1994）
BET specific surface area m²/g
146-168
HG/T3073-1999（eqv ISO 4652-1:1994）
DBP absorbing oil cm³/g
2.0-3.0
HG/T3072-1999（eqv ISO 5794-1:1994）
Total iron content mg/kg
<500
HG/T3070-1999（eqv ISO 5794-1:1994）
Standard recipe sizing material performance（150℃×10）
ISO5794/2
500% tensile stress
5.5-8.0
HG/T 2404-1992
Breaking strength Mpa
≥17.0
HG/T 2404-1992
Tensile elongation%
≥675
HG/T 2404-1992
Application
mainly applied to tire, as well as semitransparent color rubber sole, medicine carrier, and feed additive.
Note
Adjust product mesh numbers according to the user requirement.
XL228 high reinforcing, high abrasion white carbon black
Project
Technical Index
Testing Method
Whiteness
Superior or equivalent to master standard
HG/T3063-1999（eqv ISO 5794-1:1994）
Silica content(dry)%
≥90
HG/T3062-1999（eqv ISO 5794-1:1994）
Heating loss % 105℃ 2h
4.0-7.0
HG/T3065-1999（eqv ISO 5794-1:1994）
Ignition loss(dry)% 1000℃ 2h
3.0-6.0
HG/T3066-1999（eqv ISO 5794-1:1994）
PH value
5.5-7.0
HG/T3067-1999（eqv ISO 5794-1:1994）
BET specific surface area m²/g
168-188
HG/T3073-1999（eqv ISO 4652-1:1994）
DBP absorbing oil cm³/g
2.0-3.0
HG/T3072-1999（eqv ISO 5794-1:1994）
Total iron content mg/kg
<500
HG/T3070-1999（eqv ISO 5794-1:1994）
Total copper content mg/kg
<30
HG/T3068-1999（eqv ISO 5794-1:1994）
Total manganese content mg/kg
<50
HG/T3069-1999（eqv ISO 5794-1:1994）
Standard recipe sizing material performance（150℃×15）
ISO5794/2
500% tensile stress at a given elongation
5.5-8.0
HG/T 2404-1992
Breaking strength Mpa
≥17.0
HG/T 2404-1992
Elongation at failure%
≥700
HG/T 2404-1992
Application
mainly applied to radial tire, as well as sole, rubber tubes, rubber belt, solid tire, cycle tire colored tore, feed additive, medicine carrier and so on.
Note
Adjust product mesh numbers according to the user requirement.
XL328 high transparent, high reinforcing, high abrasion white carbon black
Project
Technical Index
Testing Method
Whiteness
Superior or equivalent to master standard
HG/T3063-1999（eqv ISO 5794-1:1994）
Silica content(dry)%
≥90
HG/T3062-1999（eqv ISO 5794-1:1994）
Heating loss % 105℃ 2h
4.0-8.0
HG/T3065-1999（eqv ISO 5794-1:1994）
Ignition loss(dry) % 1000℃ 2h
3.0-6.0
HG/T3066-1999（eqv ISO 5794-1:1994）
PH value
6.5-7.0
HG/T3067-1999（eqv ISO 5794-1:1994）
BET specific surface area m²/g
200-260
HG/T3073-1999（eqv ISO 4652-1:1994）
DBP absorbing oil cm³/g
3.0-3.6
HG/T3072-1999（eqv ISO 5794-1:1994）
Total iron content mg/kg
<500
HG/T3070-1999（eqv ISO 5794-1:1994）
Application
mainly applied to medicine, food, powder extinguishing agent, paint, dope, high transparent rubber .sole and so on.